Fracture Mechanics of Piezoelectric Solids with Interface Cracks

Tipo de material: TextoTextoSeries ; Fracture Mechanics of Piezoelectric Solids with Interface Cracks, 1-235, 2017Trabajos contenidos:
  • Govorukha, V
  • Kamlah, M
  • Loboda, V
  • Lapusta, Y
Recursos en línea: Resumen: Piezoelectric materials are widely used in sensors, actuators and other modern technologies. However, they are very brittle and predisposed to fracture. Appearance of cracks and interfacial failure leads to an undesired degradation of electrical and mechanical performance. This monograph is devoted to a comprehensive study of cracks situated at the interface of two piezoelectric materials. Plane electromechanical problems for piezoceramic bodies with interface cracks are analyzed.
Tags from this library: No tags from this library for this title. Log in to add tags.
Star ratings
    Average rating: 0.0 (0 votes)
Holdings
Item type Current library Collection Call number Status Date due Barcode
Documentos solicitados Documentos solicitados CICY Documento préstamo interbibliotecario Ref1 B-16531 (Browse shelf(Opens below)) Available

Piezoelectric materials are widely used in sensors, actuators and other modern technologies. However, they are very brittle and predisposed to fracture. Appearance of cracks and interfacial failure leads to an undesired degradation of electrical and mechanical performance. This monograph is devoted to a comprehensive study of cracks situated at the interface of two piezoelectric materials. Plane electromechanical problems for piezoceramic bodies with interface cracks are analyzed.

There are no comments on this title.

to post a comment.