Study on the thermal and mechanical properties of epoxy-nanoclay composites: The effect of ultrasonic stirring time

Tipo de material: TextoTextoSeries ; Materials Letters, 61(19-20)4222-4224, 2007Trabajos contenidos:
  • Wang, J
  • Qin, S
Tema(s): Recursos en línea: Resumen: Epoxy-clay nanocomposites were synthesized with organophilic montmorillonite and diglycidyl ether of bisphenol A by using the in-situ polymerization under ultrasonic treatment. The clay layers were found to be separated further with the increase in the duration of ultrasonic stirring as measured from the X-ray diffraction measurements. Thermogravimetric analysis provided the fact that the maximum thermal decomposition temperatures increased with the increase in the duration of ultrasonic stirring. However, both the glass transition temperature and the storage moduli of the composites decreased with the increase of ultrasonic stirring time as measured from the dynamic mechanical analysis
Tags from this library: No tags from this library for this title. Log in to add tags.
Star ratings
    Average rating: 0.0 (0 votes)
Holdings
Item type Current library Collection Call number Status Date due Barcode
Documentos solicitados Documentos solicitados CICY Documento préstamo interbibliotecario Ref1 B-9935 (Browse shelf(Opens below)) Available

Epoxy-clay nanocomposites were synthesized with organophilic montmorillonite and diglycidyl ether of bisphenol A by using the in-situ polymerization under ultrasonic treatment. The clay layers were found to be separated further with the increase in the duration of ultrasonic stirring as measured from the X-ray diffraction measurements. Thermogravimetric analysis provided the fact that the maximum thermal decomposition temperatures increased with the increase in the duration of ultrasonic stirring. However, both the glass transition temperature and the storage moduli of the composites decreased with the increase of ultrasonic stirring time as measured from the dynamic mechanical analysis