Kinetics of Pyrolysis and Properties of Carbon Black from a Scrap Tire

Tipo de material: TextoTextoSeries ; Chemical Papers, 60(6), p.422-426, 2006Trabajos contenidos:
  • Koreòová. A
  • Juma,M
  • Annus, J
  • Marko, J
  • Jelemensky, L
Tema(s): Recursos en línea: Resumen: The pyrolysis of rubber from the sidewall and tread of a passenger car tire was carried out in a nitrogen flow at a wide range of final temperatures. Derivative thermogravimetric analysis (DTG)was applied to examine the kinetics at the different process conditions of completed pyrolysis. Two characteristic stages were observed in the DTG curves. The first stage corresponded to the decomposition of processing oil, plastifier, and additives, whereas the rubber polymer was decomposed in the second stage. Several properties of the carbon black formed by the pyrolysis such as ash content, specific surface area, and pore size distribution were determined. A change of the internal structure of the rubber particle in the meso- and macroregions of the pore size was observed.
Tags from this library: No tags from this library for this title. Log in to add tags.
Star ratings
    Average rating: 0.0 (0 votes)
Holdings
Item type Current library Collection Call number Status Date due Barcode
Documentos solicitados Documentos solicitados CICY Documento préstamo interbibliotecario Ref1 B-10099 (Browse shelf(Opens below)) Available

The pyrolysis of rubber from the sidewall and tread of a passenger car tire was carried out in a nitrogen flow at a wide range of final temperatures. Derivative thermogravimetric analysis (DTG)was applied to examine the kinetics at the different process conditions of completed pyrolysis. Two characteristic stages were observed in the DTG curves. The first stage corresponded to the decomposition of processing oil, plastifier, and additives, whereas the rubber polymer was decomposed in the second stage. Several properties of the carbon black formed by the pyrolysis such as ash content, specific surface area, and pore size distribution were determined. A change of the internal structure of the rubber particle in the meso- and macroregions of the pore size was observed.

There are no comments on this title.

to post a comment.