Modification of epoxy resin by polysulfone to improve the interfacial and mechanical properties in glass fibre composites. II. Adhesion of the epoxy-polysulfone matrices to glass fibres

Tipo de material: TextoTextoSeries ; J. Adhesion Sci. Technol., 18(11), p.1293-1308, 2004Trabajos contenidos:
  • Brantseva, Tv
  • Gorbatkina, Y.A
  • Mader, E
  • Dutschk, V
  • Kerber, M.L
Tema(s): Recursos en línea: Resumen: Adhesion of epoxy-polysulfone (PSF)matrices to glass fibres of 12-30 ìm in diameter was studied under both quasi-static and cyclic loadings. A pull-out technique was used for adhesion measurement. It was shown that incorporation of PSF into epoxy resin changed its adhesion to fibres. A maximum was observed in the adhesion strength vs. PSF content dependence at 10 wt
Tags from this library: No tags from this library for this title. Log in to add tags.
Star ratings
    Average rating: 0.0 (0 votes)
Holdings
Item type Current library Collection Call number Status Date due Barcode
Documentos solicitados Documentos solicitados CICY Documento préstamo interbibliotecario Ref1 B-10447 (Browse shelf(Opens below)) Available

Adhesion of epoxy-polysulfone (PSF)matrices to glass fibres of 12-30 ìm in diameter was studied under both quasi-static and cyclic loadings. A pull-out technique was used for adhesion measurement. It was shown that incorporation of PSF into epoxy resin changed its adhesion to fibres. A maximum was observed in the adhesion strength vs. PSF content dependence at 10 wt