TI  - FT-IR study for hydroxyapatite/collagen nanocomposite cross-linked by glutaraldehyde
KW  - HYDROXYAPATITE
KW  - COLLAGEN
KW  - CROSS-LINKING
KW  - GLUTARALDEHYDE
KW  - FT-IR
N2  - FT-IR analysis was performed for the hydroxyapatite (HAp)/collagen (COL)nanocomposite cross-linked by glutaraldehyde (GA). The amide bands I, II and III from COL matrix, and phosphate and carbonate bands from HAp were identified. The amide B band arising from C-H stretching mode showed a sensitive conformation by the degree of cross-linking. The amide I band showed a complicate conformational change by the degree of cross-linking. The characteristic amide I band at 1685 cm?1, which is known as an aging parameter in the biological bone, did not show a monotonous tendency by the degree of cross-linking. The relative contents of the organics in the cross-linked HAp/COL nanocomposite were evaluated as an integration ratio between the amide I band at 1600-1700 cm?1 and PO43? band at 900-1200 cm?1. The increase of the organics content by the cross-linking is enabled by the further organization of Ca2+ ions of HAp crystals in HAp/COL nanocomposite. The complicate conformational behavior in the amide I, II and III bands seems to be affected by the cross-linking induced directional arrangement of HAp/COL nanocomposite fibrils
UR  - https://drive.google.com/file/d/1ytnxh61dcUNVfbMQDUC-VXAKEEI1oEPs/view?usp=drivesdk
ER  -