Solvent-free fabrication of micro-porous polyurethane amide and polyurethane-urea sca!olds for repair and replacement of the knee-joint meniscus

New porous polyurethane urea and polyurethane amide scaffolds for meniscal reconstruction have been developed in a solvent-free process. As soft segments, copolymers of 50/50 L-lactide/e-caprolactone have been used. After terminating the soft segment with diisocyanates, chain extension was performed with adipic acid and water. Reaction between the isocyanate groups and adipic acid or water provides carbon dioxide and results in a porous polymer. Extra hydroxyl-terminated prepolymer was added in order to regulate the amount of carbon dioxide formed in the foaming reaction. Furthermore, salt crystals ranging in size from 150 to 355 lm were added in order to induce macroporosity. The pore size was regulated by addition of surfactant and by the use of ultrasonic waves. The resulting porous polymer sca!olds exhibit good mechanical properties like a high-compression modulus of 150 kPa. Chain extension with adipic acid results in better mechanical properties due to better de"ned hard segments. This results from the lower nucleophilicity of carboxylic acids compared to water and alcohols. By adjusting the reaction conditions, materials in which macropores are interconnected by micropores can be obtained. On degradation only non-toxic products will be released; importantly, the materials were obtained by a simple, reproducible and solvent-free procedure.