| 245 | 1 | 0 | _aPolarized FT-IR photoacoustic spectroscopy on polymer fibers |
| 490 | 0 | _vMacroMolecular Symposia, 205(1), p.105-116, 2004 | |
| 520 | 3 | _aThe orientation of macromolecular chains in two melt-spun polymer fibers (segmented polyurethane elastomer and melt-modified polyolefine fibers)was studied by photoacoustic spectroscopy (PAS)with polarized light in the mid-infrared range. The PAS orientation functions calculated from the photoacoustic signal intensities of orientation sensitive bands describe the orientation of the different chain segments with respect to the fiber axis. Thus, the orientation of hard and soft segments in the unstressed polyurethane fiber is different and both are similiar to that of the corresponding injection molded bars. With increased spinning velocity an improved orientation of the polyolefine chains along the fiber axis, but only in the amorphous regions of the polymer, were detected. Only a slight reduction of orientation was measured as a result of the subsequent chemical crosslinking in the polyolefines. | |
| 650 | 1 | 4 | _aMOLECULAR ORIENTATION |
| 650 | 1 | 4 | _aPOLARIZED FT-IR PHOTOACOUSTIC SPECTROSCOPY |
| 650 | 1 | 4 | _aPOLYOLEFIN FIBERS |
| 650 | 1 | 4 | _aPOLYURETHANE FIBERS |
| 650 | 1 | 4 | _aPOLARIZED FT-IR PHOTOACOUSTIC SPECTROSCOPY |
| 650 | 1 | 4 | _aPOLYOLEFIN FIBERS |
| 650 | 1 | 4 | _aPOLYURETHANE FIBERS |
| 700 | 1 | 2 | _aEichhorn,K.J |
| 700 | 1 | 2 | _aAdam,G. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1sOkhjHBmrcQToU0c4NxF4DIEc_krTmK3/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c40860 _d40860 |
||