| 245 | 1 | 0 | _aPMMA/silica nanocomposite studies: Synthesis and properties |
| 490 | 0 | _vJournal of Applied Polymer Science, 91(6), p.3844-3850, 2004 | |
| 520 | 3 | _aPolymethylmethacrylate (PMMA)/silica nanocomposites are prepared by solution polymerization in this project and the resulting materials are subjected to characterization to evaluate thermal, mechanical, and fire properties. IR results show that both (3-acryloxypropyl)methydimethoxy-silane (APMDMOS)and (3-acryloxypropyl)trimethoxysilane (APTMOS)can serve as reagents for the surface modification of silica, while APTMOS performed better than APMDMOS for the modification of the silica surface. Mechanical properties of PMMA/silica nanocomposites prepared by solution blending showed decreased tensile strength and elongation at break, while materials from solution polymerization performed better than PMMA itself. Moreover, all prepared samples have shown improved thermal stabilities versus PMMA. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 91: 3844-3850, 2004 | |
| 650 | 1 | 4 | _aNANOCOMPOSITE |
| 650 | 1 | 4 | _aSURFACE MODIFICATION |
| 650 | 1 | 4 | _aPMMA |
| 650 | 1 | 4 | _aSILICA |
| 650 | 1 | 4 | _aFLAMMABILITY |
| 700 | 1 | 2 | _aYang, F. |
| 700 | 1 | 2 | _aNelson, G. L. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1ZAytD9PrJP_thsbGDmRN-_SlRWpWlsvH/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c40885 _d40885 |
||