245	1	0	_aDynamic-mechanical and dielectric relaxations of SBS block copolymer: polyaniline blends prepared by mechanical mixing
490	0		_vPolymer, 43(26), p.7505-7315, 2002
520	3		_aBlends of SBS with polyaniline doped with dodecylbenzenesulfonic acid (Pani·DBSA)or its deprotonated form (emeraldine base)were obtained by mechanical mixing and characterized by dynamical-mechanical and dielectric thermal analysis techniques. The dynamicmechanical characterization revealed that both Pani·DBSA and its non-conducting, deprotonated form exhibits different degrees of interaction with the two phases of the SBS block copolymer. The tan d peak position on temperature scale corresponding to the Tg of the PB block did not change with the addition of the conducting polymer, but there is progressive drop of peak height with the increase in Pani·DBSA concentration, probably because of the rigidity of this component. The activation energies Ea for glass-rubber transition process for both the phases of SBS were calculated using Arrhenius equation from DMTA results. From dielectric studies, it was possible to detect conductivity relaxations, at temperatures above the glass transition of the PS phase. Concerning the blend with 15 wt
650	1	4	_aSTYRENE-BUTADIENE-STYRENE
650	1	4	_aPOLYANILINE
650	1	4	_aDMTA
700	1	2	_aLeyva, M.E.
700	1	2	_aSoares, B.G.
700	1	2	_aKhastgi, D.
856	4	0	_uhttps://drive.google.com/file/d/1Mjcl8mW71SGh1Dkwk1S84-idr89CUnfT/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx
942			_2Loc _cREF1
008			250602s9999 xx |||||s2 |||| ||und|d
999			_c42707 _d42707