245	1	0	_aElectrical properties and fractal behavior of polyurethane elastomer/ polyaniline composites under mechanical deformation
490	0		_vPolymer, 48(15), p.4429-4437, 2007
520	3		_aPresent work reports on electrical properties of polyurethane elastomer/polyaniline (PU/PANIeHCl)composite films under tensile deformation. Two types of surface-modified and one type of volume-modified composite of PU and PANIeHCl were prepared. Surface modification of PU film was performed by swelling the parent film in aniline followed by its contact with the acidified oxidant solution to polymerize aniline and form ANIeHCl distributed inside surface/subsurface layer of the film. Volume-modified PU was prepared by mixing of the polymer components in a joint solution and then solution casting. Nonlinear currentevoltage characteristics were observed for surface-modified samples while linear ones were typical of volume-modified samples. Deformation of the polymer composites caused partially reversible decrease of their conductivity haracteristics, which could be described mathematically with a power law function of the strain with an exponent being dependable on the type of PU modification. Such behavior was interpreted in terms of deformation of a fractal percolation network formed in the system during its formation and chemical synthesis.
650	1	4	_aPOLYURETHANEDPOLYANILINE COMPOSITES
650	1	4	_aPERCOLATION NETWORK
650	1	4	_aNON-LINEAR ELECTRICAL PROPERTIES
700	1	2	_aHrehorova, E.
700	1	2	_aBliznyuk, V.N.
700	1	2	_aPud, A.A.
700	1	2	_aShevchenko, V.V.
700	1	2	_aFatyeyeva, K.Y.
856	4	0	_uhttps://drive.google.com/file/d/1DQOTVmRK9TPxyddW2UJGsH9jBZh5uPMn/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx
942			_2Loc _cREF1
008			250602s9999 xx |||||s2 |||| ||und|d
999			_c43127 _d43127