| 245 | 1 | 0 | _aModification of epoxy resin by polysulfone to improve the interfacial and mechanical properties in glass fibre composites. II. Adhesion of the epoxy-polysulfone matrices to glass fibres |
| 490 | 0 | _vJ. Adhesion Sci. Technol., 18(11), p.1293-1308, 2004 | |
| 520 | 3 | _aAdhesion of epoxy-polysulfone (PSF)matrices to glass fibres of 12-30 ìm in diameter was studied under both quasi-static and cyclic loadings. A pull-out technique was used for adhesion measurement. It was shown that incorporation of PSF into epoxy resin changed its adhesion to fibres. A maximum was observed in the adhesion strength vs. PSF content dependence at 10 wt | |
| 650 | 1 | 4 | _aEPOXY-POLYSULFONE MATRICES |
| 650 | 1 | 4 | _aADHESION STRENGTH |
| 650 | 1 | 4 | _aPULL-OUT TEST |
| 650 | 1 | 4 | _aQUASI-STATIC LOADING |
| 650 | 1 | 4 | _aCYCLIC LOADING |
| 700 | 1 | 2 | _aBrantseva, Tv. |
| 700 | 1 | 2 | _aGorbatkina, Y.A |
| 700 | 1 | 2 | _aMader, E. |
| 700 | 1 | 2 | _aDutschk, V. |
| 700 | 1 | 2 | _aKerber, M.L. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1zEDuwSBPd8U7s9jsMvknbNhNn4axrSmP/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c44680 _d44680 |
||