245	1	0	_aModi. cation of epoxy resin by polysulfone to improve the interfacial and mechanical properties in glass . bre composites. I. Study of processes during matrix /glass . bre interface formation
490	0		_vJ. Adhesion Sci. Technol., 17(15), p.2047-2063, 2003
520	3		_aThe rheology of epoxy resin-polysulfone blends and wetting at the blend/ glass . bre interface have been studied. Measurements were made in a rotary viscometer and in a modi. ed Wilhelmy apparatus. It was shown that none of the blends investigated revealed non-Newtonian behaviour in the range of shear rates used. The viscosity of the blends increased as polysulfone content increased. Introduction of hardener resulted in a signi. cant increase of the blends viscosity up to 2-3 orders of magnitude. Rheological tests suggested that 15 wt
650	1	4	_aEPOXY RESIN-POLYSULFONE BLENDS
650	1	4	_aRHEOLOGICAL BEHAVIOUR
650	1	4	_aBREWETTING
700	1	2	_aBrantseva, T.V.
700	1	2	_aGorbatkina, Y.A.
700	1	2	_aDutschk, V.
700	1	2	_aVogel, R.
700	1	2	_aGrundke, K.
700	1	2	_aKerber, M.L.
856	4	0	_uhttps://drive.google.com/file/d/1NV2hEi4l4pxIp58Ua1veXhhApCWT_YbK/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx
942			_2Loc _cREF1
008			250602s9999 xx |||||s2 |||| ||und|d
999			_c44681 _d44681