245	1	0	_aModification of epoxy resin by polysulfone to improve the interfacial and mechanical properties in glass fibre composites. III. Properties of the cured blends and their structures in the polymer/fibre interphase
490	0		_vJ. Adhesion Sci. Technol., 18, p.1309-1323, 2004
520	3		_aThermal and mechanical properties (linear expansion coefficient, glass transition temperatures, Young's modulus, tensile and bending strengths, and failure energies under quasistatic and impact loadings)of cured epoxy-polysulfone (PSF)blends, as well as their structures have been studied. It was shown that PSF incorporation did not lead to appreciable changes in the linear thermal expansion coefficients and glass transition temperatures of the cured blends. According to this observation, incorporation of PSF into the epoxy matrix should not result in a significant increase in the internal stresses in the system. No drop in the modulus and strength of the bulk blends was observed when compared with unmodified epoxy matrix. The failure energy of the epoxy-PSF matrices increased as the PSF content increased under all loading conditions, whereas the strength of the polymer blend matrices increased only under impact loading. Optimal PSF content was found to be 10 wt
650	1	4	_aEPOXY-POLYSULFONE BLENDS
650	1	4	_aADHESION STRENGTH
650	1	4	_aTHERMAL PROPERTIES
650	1	4	_aMECHANICAL PROPERTIES
650	1	4	_aSTRUCTURE CHARACTERIZATION
700	1	2	_aBrantseva, T.V.
700	1	2	_aGorbatkina, Y.A.
700	1	2	_aDutschk, V.
700	1	2	_aSchneider, K.
700	1	2	_aHaler, R.