245	1	0	_aPolyelectrolyte membranes for acid gas separations
490	0		_vJournal of Membrane Science, 131(1-2), p.49-60, 1997
520	3		_aNew facilitated transport membranes have been synthesized and shown to selectively permeate carbon dioxide and hydrogen sulfide from methane and hydrogen. The membranes are based on the polyelectrolyte poly(vinylbenzyltrimethylammonium fluoride), PVBTAF, and exhibit exceptional permselective properties. For example, at 23°C and 32 cmHg CO2, a PVBTAF composite membrane displayed a CO2 permeance of 6xl0-6cm3/cm2scmHg and CO2/H2 and CO2/CH4 selectivities of 87 and 1000, respectively. The CO2/H2 selectivity is the highest reported for any membrane. The permeance of both CO2 and H2S increased with decreasing feed partial pressure of the respective gases, a characteristic of facilitated transport membranes. The permselectivity is also dependent on the hydration state of the membrane and is optimal at a gas stream relative humidity in the range 0.25-0.50. The membranes show no deterioration after 30 days of continuous operation but react with trace level sulfur-containing contaminants common to cylinder H2S.
650	1	4	_aGAS SEPARATIONS
650	1	4	_aFACILITATED TRANSPORT
650	1	4	_aPOLYELECTROLYTE MEMBRANES
650	1	4	_aCARBON DIOXIDE
700	1	2	_aQuinn, R.
700	1	2	_aLaciak, D.V.
856	4	0	_uhttps://drive.google.com/file/d/1EdiVPVo9ruR53QHLhMBDNpZXpWgb1v9J/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx
942			_2Loc _cREF1
008			250602s9999 xx |||||s2 |||| ||und|d
999			_c46307 _d46307