| 245 | 1 | 0 | _aThe structure and strength of solvent welds between dissimilar amorphous thermoplastics |
| 490 | 0 | _vInternational Journal of Adhesion & Adhesives, 8(1), p.47-53, 1988 | |
| 520 | 3 | _aThe possibility of obtaining strong solvent welds between dissimilar amorphous thermoplastic adherends was investigated from studies on polyvinyl chloridepolycarbonate and polyvinyl chloride-polymethylmethacrylate solvent welds. The bonding solvents used were selected to produce gel layers of mobile polymer chains in either both or only one of the dissimilar adherends. Distinct regions were present at the original mating surfaces of the welds. Fractography and studies on the plane of failure indicated that chain interdiffusion occurred across the mating interfaces in most of the solvent welds. Solvent welds with high intrinsic and practical strength could be obtained between the dissimilar amorphous polymers. | |
| 650 | 1 | 4 | _aADHESION |
| 650 | 1 | 4 | _aADHESIVE STRENGTH |
| 650 | 1 | 4 | _aSOLVENT WELDS |
| 650 | 1 | 4 | _aTHERMOPLASTICS |
| 650 | 1 | 4 | _aGEL LAYER |
| 650 | 1 | 4 | _aMOBILE POLYMER CHAINS |
| 650 | 1 | 4 | _aSOLVENT-AFFECTED ZONE |
| 700 | 1 | 2 | _aYue, C.Y. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1p2xDDbD4M7r7hAAbk8xVRDcEmk7SlBdK/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c47540 _d47540 |
||