| 245 | 1 | 0 | _aFacile preparation of monodispersed core/shell zinc oxide@polystyrene (ZnO@PS)nanoparticles via soapless seeded microemulsion polymerization |
| 490 | 0 | _vColloids and Surfaces A: Physicochem. Eng. Aspects, 291(1-3), p.155-161, 2006 | |
| 520 | 3 | _aMonodispersed core/shell zinc oxide@polystyrene (ZnO@PS)nanoparticles with chemical bonds between the inorganic core and the polymer shell were prepared successfully by the facile soapless microemulsion polymerization of styrene (St)with the oleic acid modified zinc oxide (OA-ZnO)nanoparticles as seeds, and potassium persulphate (KPS)as initiator in water. The products were characterized by elemental analysis (EA), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM)and thermogravimetric analysis (TGA). The mechanism of the nucleation was also mentioned. The ZnO@PS nanoparticles could be well-dispersed n water and the emulsion was found to be remarkably stable. Ultraviolet-visible (UV-vis)analysis showed that the composites had high absorption in the ultraviolet region and low absorption in the visible region. | |
| 650 | 1 | 4 | _aMONODISPERSED |
| 650 | 1 | 4 | _aCORE/SHELL |
| 650 | 1 | 4 | _aZINC OXIDE@POLYSTYRENE |
| 650 | 1 | 4 | _aSOAPLESS SEEDED MICROEMULSION POLYMERIZATION |
| 650 | 1 | 4 | _aMECHANISM OF THE NUCLEATION |
| 700 | 1 | 2 | _aLiu, P. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1ZZcXQVDnLdDTOF2mp-MKte0z_5JQgA3u/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c47724 _d47724 |
||