245	1	0	_aCorrosion of graphite in industrial phosphoric acid
490	0		_vApplied Surface Science, 252(24), p.8710-8715, 2006
520	3		_aThe electrochemical corrosion of graphite in industrial phosphoric acid solutions was studied using polarisation curves analysis, cyclic voltammetry, MEB-EDS and secondary ions mass spectroscopy (SIMS). The polarisation curves indicated that graphite has a passive behaviour and the increase of temperature induces an increase of the corrosion rate and the passive current density. The cyclic voltammetry analysis was performed to verify the surface phenomenon of graphite surface and confirmed the role of adsorption oxygen in material corrosion. Spectroscopic analysis (EDS and SIMS)showed that the majority of industrial phosphoric acid impurities were present in the graphite composition indicating that metallic oxides are not the only components of this layer. The presence of these impurities on the graphite induces an increase of corrosion by swelling, exfoliation and cracking.
650	1	4	_aCORROSION
650	1	4	_aGRAPHITE
650	1	4	_aELECTROCHEMICAL ANALYSIS
650	1	4	_aCHARACTERISATION METHOD
650	1	4	_aPHOSPHORIC ACID
700	1	2	_aGuenbour, A.
700	1	2	_aIken, H.
700	1	2	_aKebkab, N.
700	1	2	_aBellaouchou, A.
700	1	2	_aBoulif, R.
700	1	2	_aBen Bachir, A.
856	4	0	_uhttps://drive.google.com/file/d/1dANsEd9GmLU2xmlrMTRK6VjBykDgu3CT/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx
942			_2Loc _cREF1
008			250602s9999 xx |||||s2 |||| ||und|d
999			_c48479 _d48479