245	1	0	_aPolylactic acid/corn cob eco-composites: Effect of new organic coupling agent
490	0		_vJournal of ThermoPlastic Composite Materials, 27(12), p.1667-1678, 2013
520	3		_aA new organic coupling agent called coconut oil coupling agent (COCA)was produced from coconut oil. The effects of filler content and COCA on mechanical, thermal, and morphological properties of corn cob (CC)-filled polylactic acid (PLA)eco-composites were studied. The results show that the addition of CC decreased the tensile strength and elongation at break but increased the modulus of elasticity of PLA/CC ecocomposites. However, the presence of COCA improved the tensile strength, elongation at break, and modulus of elasticity of PLA/CC eco-composites. Meanwhile, the glass transition temperature (Tg)of PLA/CC eco-composites was increased by increasing the CC content and COCA treatment. The peak crystallization temperature (Tc)in PLA/CC eco-composites indicated the nucleating effect of CC and the Tc of PLA/CC eco-composites decreased at 40 php of CC content. The addition of CC increased the melting temperature (Tm)of PLA/CC eco-composites but reduced the crystallinity of PLA/CC eco-composites. The COCA treatment enhanced the mechanical properties and the crystallization process of PLA/CC eco-composites. The Tc and Tm of PLA/CC eco-composites were not significantly affected by COCA treatment. The presence of COCA improved the adhesion and interaction between CC and PLA matrix.
650	1	4	_aPOLYLACTIC ACID
650	1	4	_aCORN COB
650	1	4	_aCOCONUT OIL COUPLING AGENT
650	1	4	_aECO-COMPOSITES
700	1	2	_aChun, Koay Seong
700	1	2	_aHusseinsyah, S.
856	4	0	_uhttps://drive.google.com/file/d/1A4yZ5LlafjqOte4YdxJ8xoaqORyqna7g/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx
942			_2Loc _cREF1
008			250602s9999 xx |||||s2 |||| ||und|d
999			_c48617 _d48617