| 245 | 1 | 0 | _aSynthesis of ZSM-5 zeolite with small crystal size and its catalytic performance for ethylene oligomerization |
| 490 | 0 | _vZeolites, 14(8), p.643-649, 1994 | |
| 520 | 3 | _aZSM-5 zeolites of SiO2 Al2O3 = 25 with a small crystal size were synthesized under various conditions in order to clarify a relationship between external surface area and catalytic performance, especially lifetime, for the oligomerization of ethylene to higher hydrocarbons of the gasoline range. The measurement of the external surface area, XRD patterns, and FTi.r. spectra of the resulting ZSM-5 zeolites suggested that their crystal grains were very fine. The shapes and sizes of the primary grains of the ZSM-5 zeolites were observed by means of a scanning electron microscopy with a magnification of 300,000. The crystal sizes were in the range of 30-50 nm. In the oligomerization of ethylene, a proton-type zeolite that was synthesized under a high molar ratio of OH SiO2 showed both high ethylene conversion and high gasoline range selectivity for three times longer on-stream time than those of other zeolites. The external surface area of the zeolite was also three times greater than those of other zeolites, which indicated that the lifetime of ZSM-5 zeolite in the oligomerization of ethylene depended on the external surface area or crystal size. | |
| 650 | 1 | 4 | _aCATALYST SELECTIVITY |
| 650 | 1 | 4 | _aCRYSTAL STRUCTURE |
| 650 | 1 | 4 | _aCRYSTALLIZATION |
| 650 | 1 | 4 | _aCRYSTALS |
| 650 | 1 | 4 | _aETHYLENE |
| 650 | 1 | 4 | _aGRAIN SIZE AND SHAPE |
| 650 | 1 | 4 | _aHYDROCARBONS |
| 650 | 1 | 4 | _aSCANNING ELECTRON MICROSCOPY |
| 650 | 1 | 4 | _aSURFACE MEASUREMENT |
| 650 | 1 | 4 | _aSYNTHESIS (CHEMICAL) |
| 700 | 1 | 2 | _aYamamura, M. |
| 700 | 1 | 2 | _aChaki, K. |
| 700 | 1 | 2 | _aWakatsuki, T. |
| 700 | 1 | 2 | _aOkado, H. |
| 700 | 1 | 2 | _aFujimoto, K. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1KXoGJXQmGDcpK7QmYrRoMD0BVXKNWKsY/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c50470 _d50470 |
||