| 245 | 1 | 0 | _aThe dynamic properties of carbon black loaded natural rubber vulcanizates. Part II |
| 490 | 0 | _vJournal of Applied Polymer Science, 6(21), p.368-372, 1962 | |
| 520 | 3 | _aThe dynamic shear modulus at very high strains, (G8), of carbon black filler loaded vulcanizates is regarded as due to the product of two factors: (a)a hydrodynamic interaction due to filler particles, and (b)a second factor for which evidence is given suggesting that it arises from a few strong linkages which are known to link filler particles to the matrix. Experimentally a measure of (a)has been obtained from model vulcanizates using glass spheres as the filler, and of (b)from equilibrium swelling measurements on rubber vulcanizates containing carbon black. Quantitatively, the difference between the shear modulus of the pure gum vulcanizate, Gpure gum, and G8 can be explained by these measurements. Copyright © 1962 John Wiley & Sons, Inc. | |
| 650 | 1 | 4 | _aCARBON BLACK |
| 650 | 1 | 4 | _aNATURAL RUBBER |
| 700 | 1 | 2 | _aPayne, A.R. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1y8f-rm_IkgNfiDMHJsmMcZIWSqZneF8V/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c50552 _d50552 |
||