| 245 | 1 | 0 | _aEffect of density on physical and mechanical properties of reconstituted small-sized bamboo fibrous sheet composite |
| 490 | 0 | _vAdvanced Materials Research, 150-151, p.634-639, 2011 | |
| 520 | 3 | _aThe effect of density on physical and mechanical properties of phenolic-impregnated cold-pressing reconstituted small-sized bamboo fibrous sheet composite was evaluated. The results indicated that with the density increased from 0.85g/cm 3 to 1.20 g/cm 3: water absorption decreased, thickness swelling increased first and then decreased; the value of modulus of rupture(MOR)increased from 120MPa to 230MPa, R 2 was 0.885; the value of modulus elasticity(MOE)increased from 1.8×10 4MPa to 2.8×10 4MPa, R 2 was 0.978; the shearing strength (perpendicular loading)increased from 6.5MPa to 18MPa, R 2 was 0.978;the shearing strength( parallel loading)increased from 6.3MPa to 26MPa, R 2 was 0.973;the compression parallel to grain values increased from 80MPa to 120MPa. | |
| 650 | 1 | 4 | _aCOLD-PRESSING |
| 650 | 1 | 4 | _aDENSITY |
| 650 | 1 | 4 | _aPHYSICAL AND MECHANICAL PROPERTIES |
| 650 | 1 | 4 | _aRECONSTITUTED BAMBOO FIBROUS SHEET COMPOSITE |
| 650 | 1 | 4 | _aSMALL-SIZED BAMBOO |
| 700 | 1 | 2 | _aZhu, R. |
| 700 | 1 | 2 | _aYu, W. |
| 856 | 4 | 0 |
_uhttps://drive.google.com/file/d/1L4zNjWNBR_K3Ol_QCRZMIUUmGuK5LP4p/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx |
| 942 |
_2Loc _cREF1 |
||
| 008 | 250602s9999 xx |||||s2 |||| ||und|d | ||
| 999 |
_c50891 _d50891 |
||