245	1	0	_aInterfacial shear strength of flax fibers in thermoset resins evaluated via tensile tests of UD composites.
490	0		_vInternational Journal of Adhesion & Adhesives, 36, p.39-43, 2012
520	3		_aA method of interfacial shear strength evaluation, based on the length distribution of fibers pulled out from the tensile fracture surface of an oriented flax-reinforced composite, is applied to composites with vinyl ester and acrylated epoxidized soy oil resin matrices. Two approaches for characterizing the strength of fibers with modified Weibull distribution, fiber fragmentation tests and fiber tension tests, are compared in the analysis of pull-out data. Interfacial shear strength is found to increase by a few percent when loading rate is increased from 1.33 percent to 8 percent/min.
650	1	4	_aFLAX FIBERS
650	1	4	_aINTERFACIAL SHEAR STRENGTH
650	1	4	_aPOLYMER MATRIX COMPOSITE
700	1	2	_aSparnins, E.
700	1	2	_aNyström, B.
700	1	2	_aAndersons, J.
856	4	0	_uhttps://drive.google.com/file/d/17w-7IuwyVx0vTMyhloeYUuPw67tHo4mm/view?usp=drivesdk _zPara ver el documento ingresa a Google con tu cuenta: @cicy.edu.mx
942			_2Loc _cREF1
008			250602s9999 xx |||||s2 |||| ||und|d
999			_c52407 _d52407